Overview of POE Elastomer = = POE POE for Poly real Olefin Elastomer shorthand, namely ene 桱 class generally said POE Elastomer say representatives of PE as hard segment of Elastomer, and PP as hard segment of elastomers including called TPO and TPV this several manufacturers: POE manufacturers: At present, POE is only produced by four manufacturers in the world: none of them are currently produced in China, so all of them must rely on the entrance Engage. DOW Engage. Infuse Exxon Exact MITSUI Tafma Seetec. LG Seetec. Main use: POE main use: 1. As plastic flexibilizer, including Nylon, PP, PE toughening agent (2) as a foam material at present this two kinds of use are low density low liquidity of POE specifications better generally want to MI in 0.5 ~ 6 low density low, liquidity, between, the lower the better, the density of about 0.87 or so, hard segment (PE) ratio is too high, too high said between toughening, the lower the better effect of soft segment is too little, toughening or grafting effect is poorer.

  POE elastomers are generally divided into eight carbons and four carbons. Hardness and toughness of eight carbons are better than that of four carbons. Therefore, generally eight carbons are used as the main graft materials. POE (1) the United States dupont. 7256.7340.7467.8150.8200 8401.8402.8480.8999 (2) the POE dow 8999.8150.5501.8003.8100.8180.8407 POE (3) the United States exxon 5061 VM - 6202.5062.5171.5371 mitsui DF710. (4) the POE Singapore DF740. DF810. DF840 (5) the POE Japanese mitsui chemicals 4085, DF640 DF710 DF740, DF - 840, DF940 TA610, TA640, TA710 (6) POE South Korea LG, LC170, LC670 P0E processing usually thermoplastic plastics processing equipment used for processing molding. Molding temperature and processing pressure should be slightly higher, can be processed at extremely high processing speed. Can be injection molding, extrusion molding, can also be used to process a calender plate or film, and can be blown molding, using heat molding can be made of complex shape products. According to the need to add a variety of pigments to make different colors.

Performance index of POE elastomer

Around  

Performance Indicators

Density（ g/cm 3 ）
0.852-0.880
Melting Point（℃）
50—70
100%Modulus（MPa）
1.0-5.2
Shore Hardness（ A）
65—85
Flexural Modulus（ Mpa）
8.0-28.0
Melt Index（ dg/min）
0.5—30+
Long Stretch Rate（%）
700-1000+
Low Temperature Brittleness（℃）
<-76
POE has many advantages over some traditional elastomers：
Contrast EPDM
Contrast SBS
Contrast EVA，EMA，EEA
Contrast with soft PVC

Excellent weld strength

Good dispersity

Equal amount of added impact strength is high

Outstanding molding ability

Easy to operate

Good weathering resistance

High transparency

Low price

Light weight
Good toughness

Good flexural

No special equipment required

Low corrosion to equipment

Good thermal molding

The plastic is good

Better brittleness at low temperature

Good economy